Microstructure and Mechanical Properties of Al-Cu-Mg-Ag Alloy during Thermal Exposed at Elevated Temperature
Liu, Xiao Yan; Pan, Qing Lin; Lu, Zhi Lun; Cao, Su Fang; He, Yun Bin; Li, Wen Bin
Authors
Qing Lin Pan
Zhi Lun Lu
Su Fang Cao
Yun Bin He
Wen Bin Li
Abstract
The thermal stability of Al-Cu-Mg-Ag alloys under-aged and peak-aged was analyzed by tensile testing and transmission electron microscopy (TEM). And the microstructural evolution and mechanical properties of Al-Cu-Mg-Ag alloy during thermal exposed at elevated temperature were also studied. The results show that the under-aged Al-Cu-Mg-Ag alloy possessed better thermal stability compared with the peak-aged alloy when exposed at 150 . The tensile strength of the peak-aged alloy decreased with prolonging the holding time. While that of the under-aged alloy increased and then decreased with a peak of 524 MPa after exposed for 20 h, which was 19 MPa higher than that of the peak-aged alloy. Meanwhile the precipitations were distributed dispersively and amount of fine phases were observed. The tensile strength of the under-aged alloy was 434 MPa after exposed for 1000 h at 150 . When exposed at 200 , the tensile strength of the under-aged sample decreased and the prolongation increased with prolonging the thermal exposure time. The tensile strength of the sample decreased dramatically when exposed at 250 and 300 and the strengthening phases coarsened dramatically and evolved to the equilibrium phases . The width of the precipitation free zone (PFZ) increased with increasing the thermal exposure temperature and the distribution of the precipitations on the boundaries became discontinuous.
Journal Article Type | Article |
---|---|
Publication Date | 2010-10 |
Deposit Date | Oct 23, 2021 |
Journal | Advanced Materials Research |
Print ISSN | 1022-6680 |
Publisher | Trans Tech Publications |
Peer Reviewed | Peer Reviewed |
Volume | 152-153 |
Pages | 1426-1436 |
DOI | https://doi.org/10.4028/www.scientific.net/amr.152-153.1426 |
Keywords | Al-Cu-Mg-Ag Alloy, Microstructural Evolution, Thermal Exposure, Under-Aged |
Public URL | http://researchrepository.napier.ac.uk/Output/2815974 |
You might also like
High-Figure-of-Merit Thermoelectric La-Doped A-Site-Deficient SrTiO3 Ceramics
(2016)
Journal Article
Field-induced quantum spin disordered state in spin-1/2 honeycomb magnet Na2Co2TeO6
(2021)
Journal Article
Microstructure and electrical properties of Nb‐doped SrTiO3‐BiFeO3 based lead‐free ceramics
(2021)
Journal Article
Electroceramics for High-Energy Density Capacitors: Current Status and Future Perspectives
(2021)
Journal Article
Downloadable Citations
About Edinburgh Napier Research Repository
Administrator e-mail: repository@napier.ac.uk
This application uses the following open-source libraries:
SheetJS Community Edition
Apache License Version 2.0 (http://www.apache.org/licenses/)
PDF.js
Apache License Version 2.0 (http://www.apache.org/licenses/)
Font Awesome
SIL OFL 1.1 (http://scripts.sil.org/OFL)
MIT License (http://opensource.org/licenses/mit-license.html)
CC BY 3.0 ( http://creativecommons.org/licenses/by/3.0/)
Powered by Worktribe © 2024
Advanced Search