Electrodeposition and characterisation of Ni/gelatin microgels coatings

Gibb, A.; Vorobjovs, A.; Jagoda, Z.; Winiarski, J.; Stankiewicz, A.

Abstract

This work focuses on implementing microgels for carrying self-healing substances in protective coatings. Ni/gelatin microgels coatings were manufactured using electroplating techniques. Microscopic analysis was carried out to establish the presence of microgels in the coating. This was followed by an investigation into the influence of the microgels on the mechanical properties and corrosion resistance of the coatings. The composite Ni/gelatin microgels coating exhibited better wear resistance and higher hardness than the plain nickel coating. Electrochemical impedance analysis showed the difference in the corrosion behaviour of the coatings in 3.5 wt. % NaCl solution. Over the time of the immersion, the corrosion resistance of the nickel coatings decreased from 28 to 14 kΩ cm2, while the composite coatings increased from 5.8 to 10 kΩ cm2. At this stage of the research, only microgels without any active compounds have been used, thus no information related to the self-healing characteristics of coatings is currently available.

Citation

Gibb, A., Vorobjovs, A., Jagoda, Z., Winiarski, J., & Stankiewicz, A. (2020). Electrodeposition and characterisation of Ni/gelatin microgels coatings. Transactions of the Institute of Metal Finishing, 98(1), 15-20. https://doi.org/10.1080/00202967.2020.1692528

• Journal Article Type: Article
• Acceptance Date: Oct 16, 2019
• Online Publication Date: Jan 9, 2020
• Publication Date: Jan 2, 2020
• Deposit Date: Jan 10, 2020
• Publicly Available Date: Jan 3, 2021
• Journal: Transactions of the IMF
• Print ISSN: 0020-2967
• Electronic ISSN: 1745-9192
• Publisher: Taylor & Francis
• Peer Reviewed: Peer Reviewed
• Volume: 98
• Issue: 1
• Pages: 15-20
• DOI: https://doi.org/10.1080/00202967.2020.1692528
• Keywords: Nickel composite coating, self-healing, microgel, gelatin, corrosion, electrodeposition
• Public URL: http://researchrepository.napier.ac.uk/Output/2465360